Morphological evolution and selection of angular primary silicon is investigated in near-eutectic Al-Si alloys. Angular silicon arrays are grown directionally in a Bridgman furnace at velocities in the regime of 10-3 m/sec and with a temperature gradient of 7.5x103 K/m. Under these conditions, the primary Si phase grows as an array of twinned bicrystalline dendrites, where the twinning gives rise to a characteristic 8-pointed star-shaped primary morphology. While this primary Si remains largely faceted at the growth front, a complex structure of coherent symmetric twin boundaries enables various adjustment mechanisms which operate to optimize the characteristic spacings within the primary array. In the work presented here, this primary silicon growth morphology is examined in detail. In particular, this thesis describes the investigation of (1) morphological selection of the twinned bicrystalline primary starshape morphology; (2) primary array behavior, including the lateral propagation of the starshape grains and the associated evolution of a strong <100> texture; (3) the detailed structure of the 8-pointed star-shaped primary morphology, including the twin boundary configuration within the central core; (4) the mechanisms of lateral propagation and spacing adjustment during array evolution; and (5) the thermosolutal conditions (i.e. operating state) at the primary growth front, including composition and phase fraction in the vicinity of the primary tip;Experimental methods include directional solidification, high-resolution serial milling, electron-probe microanalysis, backscattered electron diffraction, and high resolution transmission electron microscopy techniques. The following key observations are made here;1. It is found that slightly hypereutectic Al-Si alloys, directionally solidified at rate below 1mum/s, exhibit rapid emergence of a strong <100> texture, associated with the selection and lateral propagation of the star-shaped growth mode. The dominant silicon morphology in this array is an 8-pointed star-shape "dendrite" with sideplates at alternating angles of 37° and 53°. Large domains of identically oriented silicon dendrites evolve, suggesting that the entire twinned domain originates from one twin-pair of silicon grains;2. Analysis of the detailed structure within the twinned core reveals that 210/310 coherent twin boundaries comprise the core structure of the 8-pointed star-shape. These crystal defects, with a high migration tendency, provide the core with an essential mechanism for the faceted interfaces to grow. Thus, the twin structure plays a crucial role in the morphological/mechanistic selection of the primary silicon morphology in these Al-Si alloys at low grow rates;3. Examination of the overall array structure and dynamics with regard to several mechanisms of branching and spacing adjustment shows that primary tip splitting/joining, tertiary branching, and related twin boundary migration in the core are the main mechanisms for array evolution. Although the Al phase has no preferred orientation with respect to the axial growth direction, its grain structure seems to be influenced by the side branching of silicon, resulting in the polycrystalline grains with no more than one grain between two silicon secondary plates;4. Primary and inter-plate spacing have been measured and the result suggests that overall growth is a diffusively coupled "cellular" growth. In order to model the overall low-velocity growth of Al-Si alloys, which have a kinetically limited twinned Si array, we propose a "mesoscopic" envelope and some relevant experiments such as corner growth experiments and directional growth at hypoeutectic compositions for the quantification of supersaturaton and tip temperature, combining with phase fraction measurements near the primary tip;Through the observations and analyses highlighted above, the growth of the faceted silicon bycrystalline structure in near eutectic Al-Si has been comprehensively understood. Phase fraction, composition, interface structure, and spacing in the interdendritic region behind the growing tip suggest that overall microstructure evolution occurred by a very tiny decoupled primary tip, followed by an Al "halo-like" structure surrounding the silicon star-shape. Overall microstructure evolution proceeds with the assistance of crystal defects (i.e. twinning in the silicon dendrite core) and this mechanistic self-optimization by twinning allows the strongly anisotropic faceted crystal-melt interfaces to respond to local fluctuations, selecting the distinct star-shaped silicon morphology which best satisfy long-range diffusion fields.