Short range order structrures of lithium oxy-thiosilicophosphate glasses
Date
2023-09
Authors
Major Professor
Advisor
Committee Member
Journal Title
Journal ISSN
Volume Title
Publisher
Elservier B.V.
Abstract
In this work, the compositional series of sulfide and mixed oxysulfide (MOS) glasses 0.56Li2S + 0.44[(0.33-x)PS5/2 + xPO5/2 + 0.67SiS2] was prepared, where 0 ≤ x ≤ 0.33, and their short range order (SRO) structures and their thermal properties have been investigated. Powder x-ray diffraction (XRD) confirmed that the MOS glasses were free from crystallization, with only very minor diffraction peaks in the x = 0 glass being observed. Fourier transform infrared (FT-IR), Raman, and 29Si and 31P magic angle spinning (MAS) NMR spectroscopies were used to identify the SRO structures present in these glasses. These spectra revealed oxygen migration from P to Si during synthesis. Although oxygen was introduced in the form of phosphorus oxide, the majority of the oxygen in these glasses ends up being bonded to silicon, thereby creating sulfur-rich SROs centered by phosphorus and MOS SROs centered by silicon. It was further found that the P-S SRO species were predominantly charged non-bridging sulfurs (NBS). The Si SRO species were comprised of neutral bridging oxygens (BOs) and charged non-bridging oxygens (NBOs) and neutral bridging sulfurs (BS) and charged non-bridging sulfurs with the neutral BO and BS species being larger in fraction than the NBO and NBS. These results suggest that the preponderance of the mobile Li+ cations in these glasses are located near the more negatively charged P centers and not near the more neutrally charged Si centers. The average negative charge of the P SRO structures was found to be ∼ − 3.0 with ∼97% of the phosphorous species in the P0 SRO while the average negative charge of the Si SRO structures was found to be −2.3. Consistent with the creation of the large numbers of NBS on the P and more BOs and BSs on the Si, these values are more negative and more positive, respectively, than the compositionally expected average value of −2.55. Differential scanning calorimetry (DSC) measurements of their glass transition (Tg) and crystallization (Tc) temperatures showed that the Tgs of these glasses are higher than 300 °C and their working ranges, ΔT ≡ Tc – Tg, are ∼100 °C.
Series Number
Journal Issue
Is Version Of
Versions
Series
Academic or Administrative Unit
Type
article
Comments
This article is published as Hu, G., Torres III, V.M., Martin, S.W., Short range order structrures of lithium oxy-thiosilicophosphate glasses. Journal of Non-Crystalline Solids: X; 19(September 2023);100198. https://doi.org/10.1016/j.nocx.2023.100198. Posted with permission.
© 2023 The Authors
https://creativecommons.org/licenses/by-nc-nd/4.0/
© 2023 The Authors
https://creativecommons.org/licenses/by-nc-nd/4.0/