Synthesis and characterization of hydrated alkali thio-hydroxosilicogermanates of the form, Rb[subscript z](Ge[subscript x]Si₁[subscript x])S[subscript z](OH)₄[subscript z] ·yH₂O where 2[less than or equal to]z[less than or equal to]3 and 0.5[less than or equal to]x[less than or equal to]1.0

Thumbnail Image
Nelson, Carly
Major Professor
Committee Member
Journal Title
Journal ISSN
Volume Title
Research Projects
Organizational Units
Journal Issue
Is Version Of

Research into fuel cell technology has increased dramatically recently due to the increasing gas prices and stricter pollution regulations. The need for a high proton conducting and thermally stable electrolyte for intermediate temperature (~100-300 °C) fuel cells has become a critical problem for proton exchange membrane (PEM) fuel cells in order to replace the present automobile internal combustion engines. Nafion is currently a very popular polymer electrolyte material with a proton conductivity of ~10⁻⁰̇·⁷⁷ ([Omega]cm)⁻¹ at 80 °C under heavily hydrated conditions. At temperatures above ~80 °C, Nafion dries out and its proton conductivity decreases to essentially zero. Research at ISU into alternative ceramic membranes for PEMs resulted in the development of alkali thio-hydroxogermanates (M[subscript x]GeS[subscript x](OH)₄[subscript x]·yH₂O where M=Na, K, Rb, Cs) with high proton conductivities of ~10⁻² ([Omega]cm)⁻¹ at 120 °C and thermal stabilities up to ~300 °C. In an effort to further increase the proton conductivity, especially at temperatures near room temperature and to increase the long term thermal stability, new ternary alkali thio-hydroxosilicogermanates where Si⁴ has been partially substituted for Ge⁴⁺ to form compositions of the form Rb[subscript z]Ge[subscript x]Si[subscript 1-x]S[subscript z](OH)[subscripr 4-z]·yH₂O, where z=2 and 3, and 0.5[less than or equal to]x[less than or equal to]1.0, have been prepared and characterized for the first time. It was found that the Ge-based phases were observed to have higher intermediate temperature proton conductivities than the Ge/Si phases. Studies were conducted on the proton conductivity as a function of the relative humidity and it was found that even low levels of hydration (~6% R.H.) greatly improved the proton conductivity at low temperatures indicating the important role of water in the proton conduction mechanism.

Sun Jan 01 00:00:00 UTC 2006